Optical properties and radiation stability of SiO2/ZnO composite pigment prepared by co-sintering method

Thermal control coatings (TCCs) are an essential part of the thermal control systems in the spacecraft. Solar absorptance and emittance are the key performance parameters of TCCs. To develop an ultra-low solar absorption and stable inorganic TCCs for surface radiator, different TCCs were prepared by co-sintering ZnO and SiO₂ nanoparticles to form Zn₂SiO₄/SiO₂ pigment in this work, and the optical properties and radiation stability were systematically studied. It is found that the coating based on composite pigment has high reflectivity in the ultraviolet band and excellent optical performance possessing the low solar absorption of 0.06. In addition, the Zn₂SiO₄/SiO₂ coating demonstrates the highest proton and electron radiation stability because that SiO₂ between Zn₂SiO₄ particles acts as the relaxation center of the defects caused by radiation.     

Preparation,microstructure and ion-irradiation damage behavior of Al4SiC4-added SiC ceramics

Single-phase Al₄SiC₄ powder with a low neutron absorption cross section was synthesized and mixed with SiC powder to fabricate highly densified SiC ceramics by hot pressing. The densification of SiC ceramics was greatly improved by the decomposition of Al₄SiC₄ and the formation of aluminosilicate liquid phase during the sintering process. The resulting SiC ceramics were composed of fine equiaxed grains with an average grain size of 2.0 μm and exhibited excellent mechanical properties in terms of a high flexure strength of 593 ± 55 MPa and a fracture toughness of 6.9 ± 0.2 MPa m^1/2. Furthermore, the ion-irradiation damage in SiC ceramics was investigated by irradiating with 1.2 MeV Si⁵⁺ ions at 650 °C using a fluence of 1.1 × 10¹⁶ ions/cm², which corresponds to 6.3 displacements per atom (dpa). The evolution of the microstructure was investigated by X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy. The breaking of Si–C bonds and the segregation of C elements on the irradiated surface was revealed by XPS, whereas the formation of Si–Si and C–C homonuclear bonds within the Si–C network of SiC grains was detected by Raman spectroscopy.     

A kinetic model involving oxidation and volatilization in SiC-B4C-xAl2O3 ceramics system

In this paper, a new kinetic model considering both oxidation and volatilization kinetics is established and applied to analyze the oxidation of SiC-B₄C-xAl₂O₃ ceramics and other systems in various oxidation conditions. The effects of diffusion area and volume changes during the oxidation process are considered in this model. The physical meaning of each parameter in this model is explicit and simple. According to this model, the diffusion coefficient of species and the corresponding diffusion activation energy are easily available. The practicability of this model is well verified by the experimental data of SiC-B₄C-xAl₂O₃ and other systems oxidized under different conditions. In addition, the practice shows that the model is applicable not only to the systems where oxidation and volatilization coexist, but also to the system where only oxidation plays a major role. We hope the model proposed in this work can be used in other materials with more complex environments.     

Preparation of high-purity SiC ceramics with good plasma corrosion resistance by hot-pressing sintering

High-purity SiC ceramic devices are applied in semiconductor industry owing to their outstanding properties. Nevertheless, it is difficult to densify SiC ceramics without any sintering additive even by HP sintering. In this work, high-purity and dense SiC ceramics were fabricated by HP sintering with very low amounts of sintering aids. Residual B content was only 556 ppm and relative density was more than 99.5%. Furthermore, thermal conductivity of as-prepared SiC ceramics was improved from 155 W m^?1 K^?1 to 167 W m^?1 K^?1 by increasing holding time and their plasma corrosion resistance was promoted in the meantime. The as-prepared high-purity SiC ceramics have broad application prospects in the field of semiconductor industry.     

Highly oriented α-Al2O3 transparent ceramics shaped by shear force

Alumina platelets were arranged horizontally in submicron alumina particles by shear force in the flow of slurries during casting. The obtained alumina green bodies with platelets were pressureless-sintered in vacuum, producing ceramics with thoroughly oriented grains and high transmittance. The effects of sintering parameters on the densification, microstructure evolution, and orientation degree of alumina ceramics were investigated and discussed. The results showed that the densification, grain size, orientation degree, and in-line transmittance were increased with increasing sintering temperature. The enhancement of orientation degree was mainly coherent with grain growth. The grain-oriented samples exhibited a much higher in-line transmittance (at 600 nm) of 61 % than that of the grain random sample (29 %). Moreover, the transmission remained a high level in the ultraviolet range (<300 nm).     

锡量子点制备及其电催化还原二氧化碳产甲酸性能

锡基材料在自然界含量丰富、价格低廉, 在电催化还原CO₂制液体燃料反应中具有巨大潜力。但是较低的产物选择性和较差的稳定性限制了其应用。本工作制备的锡量子点电催化剂(Sn-QDs), 具有高效、高稳定性和高选择性的电催化还原CO₂产HCOOH活性。Sn-QDs的平均颗粒尺寸仅为2~3 nm, 结晶性良好。小的颗粒尺寸增大了电化学活性面积(ECSA), Sn-QDs的ECSA约为锡颗粒的4.4倍。ECSA增大以及CO₂还原反应动力学加速, 促进了CO₂电化学转化。在-1.0 V (vs RHE)下, Sn-QDs/CN催化剂的HCOOH法拉第效率(FE_HCOOH)达到95%, 并且在宽约0.5 V的电势范围内能够保持在83%以上。此外, Sn-QDs/CN可以在24 h内保持良好的电化学稳定性。     

Strong tribocatalysis of strontium titanate nanofibers through harvesting friction energy for dye decomposition

Friction is a common clean energy and can be harvested and converted into electricity energy via triboelectricity, which can electrochemically drive dye decomposition in theory. In this work, the tribocatalytic Rhodamine B dye decomposition has been experimentally realized in strontium titanate (SrTiO₃) nanofibers, which are synthesized via a hydrothermal method. In the tribocatalytic dye decomposition process, the friction is exerted in the interface between catalyst surface and a polytetrafluoroethylene (PTFE) Teflon rod setup with the different stirring speed. The RhB dye decomposition ratios of SrTiO₃ nanofibers at these stirring speeds of 200 rpm, 400 rpm, 600 rpm, and 800 rpm are respectively 24.2%, 51.8%, 73.9% and 88.6%, yielding to these reaction rate constants of ～0.0112 h^?1, ～0.0260 h^?1, ～0.0562 h^?1 and ～0.0877 h^?1. The main active species, which play an important role in tribocatalytic process, are the superoxide radicals and holes on basis of the active species quenching experiment results. The excellent tribocatalysis activity makes SrTiO₃ nanofibers potential for application in dye wastewater treatment through utilizing the environmental friction energy.     

(1-x)Bi0.5Na0.47Li0.03TiO3-xNaNbO3 lead-free ceramics with superior energy storage performances and good temperature stability

Dielectric capacitors show great potential in superior energy storage devices. However, the energy density of these capacitors is still inadequate to meet the requirement of energy storage applications. In this study, the Bi_0.5Na_0.47Li_0.03TiO₃-xNaNbO₃ (BNLT-xNN) ceramics were prepared via conventional solid-phase reaction. Results showed that NN can efficaciously enhance the breakdown strength (E_b) and the relaxation behavior of the BNLT ceramic because of the broken ferroelectric long-range order. When x = 0.3, the maximum E_b reached 350 kV/cm, at which the 0.7BNLT-0.3NN ceramic exhibited the high recoverable energy storage density (W_rec) of 4.83 J/cm³ and great efficiency (η) of 78.9%. The ceramic demonstrated good temperature stability at 20 °C-160 °C and excellent fatigue resistance. Additionally, the 0.7BNLT-0.3NN ceramic presented high power density (P_D; ～77.58 MW/cm³), large current density (C_D; ～861.99 A/cm²), and quite short discharge time (t_0.9; ～0.090 μs). These results indicated that the 0.7BNLT-0.3NN material has excellent energy storage properties and various application prospects.     

Synthesis of transparent YIG ceramics by pressureless sintering

Transparent YIG (Y₃Fe₅O₁₂) ceramics are successfully synthesized by reactive sintering at normal pressure using γ-Fe₂O₃ and Y₂O₃ as starting materials. The grain size of the sintered YIG ceramics is ca. 10–15 µm. Residual pores are not observed on the surface of sample, but numerous residual pores are observed by infrared transmission microscopy. In-line transmittance of a commercially available high-quality YIG single crystal (thickness 1 mm) fabricated by the floating zone method is 75 % in the near to mid-infrared region, whereas the sample produced in this study shows an in-line transmittance of 71 % in the wavelength range above 1.5 µm.